X5CrNi18-10 - (1.4301) / SUS 304 / X5CrNi18-9 / 301S21 / 0Cr18Ni9 / 17240 / 725
X5CrNi18-10 - 1.4301
Application Information
Grade (EU) | X5CrNi18-10 |
Number | 1.4310 |
Density | 7.9 g/cm³ |
USA | 304 - 304N |
Germany, DIN | X5CrNi18-9 |
Japan, JIS | SUS304 |
France, ANFOR | X5CrNi18-10
Z5CN18-09 Z6CN18-09 Z7CN18-09 |
England, BS | 301S21
302S26 |
Italy, UNI | X5CrNi18-10 |
China, GB | 0Cr18Ni9 |
Sweden, SS | 2333-02 |
Poland, PN | 0H18N9 |
Czechia, CSN | 17240 |
Finland, SFS | 725 |
Austria, ONORM | X5CrNi18-10S |
EN 10088-2: 2005 |
EN 10088-3: 2005 |
EN 10028-7: 2007 |
EN 10222-5: 2000 |
EN 10151: 2003 |
EN 10216-5: 2014 |
EN 10217-7: 2005 |
EN 10296-2: 2005 |
EN 10253-3: 2008 |
EN 10253-4: 2008 |
EN 10269-4: 1999 |
EN 10272: 2007 |
EN 10263-5: 2001 |
EN 10250-4: 2000 |
EN 10297-2: 2005 |
EN 10088-4: 2009 |
EN 10088-5: 2009 |
C | MAX 0.07 |
Si | max 1.00 |
Mn | max 2.00 |
Ni | 8 - 10.5 |
P | max 0.045 |
S | max 0.015 |
Cr | 17.5 - 19.5 |
N | max 0.11 |
Rm - Tensile strength (MPa) (+A) | 500 - 750 |
Rm - Tensile strength (MPa) (+AT) | 500 - 700 |
Rm - Tensile strength (MPa) (+AT+C) | 780 - 820 |
Rp0.2 0.2% proof strength (MPa) (+At) | 195 |
Rp0.2 0.2% proof strength (MPa) (+A) | 190 - 235 |
KV - Inpact energy (J) transverse (+A) | +20° - 60 | -196° - 60 |
KV - Inpact energy (J) longitud (+A) | +20° - 100 |
A - Min. elongation at fracture (%) (+A) | 35 - 45 |
A - Min. elongation at fracture (%) longitud | 40 |
Vickers hardness (HV) (+CR): | 220 - 450 |
Brinell hardness (HB) (+A): | 215 |
Brinell hardness (HB) (+AT): | 200 |