Equivalent References
Corrosion-resistant, Steel chassis, metal temperature below -196 ° C is also not applicable.
Public Id
X2CrNiMo17-12-3 - (1.4432)
Grade (EU) |
X2CrNiMo17-12-3 |
Number |
1.4432 |
USA |
316L |
Japan, JIS |
SUS316L |
France, ANFOR |
Z3CND17-13-03
Z3CND18-14-03 |
England, BS |
316S13 |
Sweden, SS |
2353 |
Russia, GOST |
03KH17N14M3 |
Standards
X2CrNiMo17-12-3 - (1.4432)
EN 10088-2: 2005 |
EN 10088-3: 2005 |
EN 10028-7: 2007 |
EN 10222-5: 2000 |
EN 10217-7: 2005 |
EN 10296-2: 2005 |
EN 10253-3: 2008 |
EN 10253-4: 2008 |
EN 10272: 2007 |
EN 10263-5: 2001 |
EN 10088-1: 2005 |
EN 10088-5: 2009 |
EN 10088-4: 2009 |
Chemical Composition
X2CrNiMo17-12-3 - (1.4432)
C |
max 0.03 |
Si |
max 1.00 |
Mn |
max 2.00 |
Ni |
10.5 - 13 |
P |
max 0.045 |
S |
max 0.015 |
Cr |
16.5 - 18.5 |
Mo |
2 - 2.50 |
N |
max 0.11 |
Mechanical Properties
X2CrNiMo17-12-3 - (1.4432)
Rm - Tensile strength (MPa) (+A) |
490 - 700 |
Rm - Tensile strength (MPa) (+AT) |
490 - 690 |
Rm - Tensile strength (MPa) (+AT+C) |
750 - 780 |
X2CrNiMo17-12-3 - (1.4432)
Rp0.2 0.2% proof strength (MPa) (+AT) |
190 - 240 |
Rp0.2 0.2% proof strength (MPa) (+A) |
190 |
X2CrNiMo17-12-3 - (1.4432)
KV - Impact energy (J) transverse, (+A) |
+20° - 60 |
+196° - 60 |
KV - Impact energy (J) longitud., (+A) |
+20° - 100 |
X2CrNiMo17-12-3 - (1.4432)
A - Min. elongation at fracture (%) (+A) |
40 - 45 |
A - Min. elongation at fracture (%) longitud (+AT) |
40 |
X2CrNiMo17-12-3 - (1.4432)
Nominal diameter(mm) |
2 - 50 |
Z - Reduction in cross section on fracture (%) |
63 - 68 |
X2CrNiMo17-12-3 - (1.4432)
Brinell hardness (HB) (+A): |
215 |
Brinell hardness (HB) (+AT): |
200 |