X6CrNiMoTi17-12-2 - (1.4571)/X6CrNiMoTi17-12-2/X10CrNiMoTi18-10/SUS316Ti/Z6CNDT17-12/H17N13M2T

X6CrNiMoTi17-12-2 - 1.4571

Uygulama Bilgileri


Genel Kimliği

X6CrNiMoTi17-12-2 - 1.4571

Grade (EU) X6CrNiMoTi17-12-2
Number 1.4571
USA 316Ti
Germany, DIN X10CrNiMoTi18-10
X6CrNiMoTi17-12-2
Japan, JIS SUS316Ti
France, ANFOR Z6CNDT17-12
Z6CNT17-12
England, BS 320S31
321S12
Italy, UNI X6CrNiMoTi17-12
China, GB 0Cr18Ni12Mo2Ti
1Cr18Ni12Mo2Ti
Sweden, SS 2350-02
Poland, PN H17N13M2T
Czechia, CSN 17348
Finland, SFS 761
Austria, ONORM X6CrNiMoTi17-12-2S
Russia, GOST 08KH17N13M2T
10KH17N13M2T

Standartları

X6CrNiMoTi17-12-2 - 1.4571

EN 10088-2: 2005
EN 10088-3: 2005
EN 10028-7: 2007
EN 10222-5: 2000
EN 10216-5: 2014
EN 10217-7: 2005
EN 10296-2: 2005
EN 10253-3: 2008
EN 10253-4: 2008
EN 10272: 2007
EN 10263-5: 2001
EN 10250-4: 2000
EN 10297-2: 2005
EN 10088-1: 2005
EN 10088-4: 2009
EN 10088-5: 2009

Kimyasal Kompozisyonu

X6CrNiMoTi17-12-2 - 1.4571

C max 0.08
Si max 1.00
Mn max 2.00
Ni 10.5 - 13.5
P max 0.045
S max 0.015
Cr 16.5 - 18.5
Mo 2 - 2.5
Ti max 0.70

Mekanik Özellikleri

X6CrNiMoTi17-12-2 - 1.4571

Rm - Tensile strength (MPa) (+A) 500 - 700
Rm - Tensile strength (MPa) (+AT+C) 810 - 850
Rm - Tensile strength (MPa) (+AT) 500 - 730

X6CrNiMoTi17-12-2 - 1.4571

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+AT) 190 - 210
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 200 - 240

X6CrNiMoTi17-12-2 - 1.4571

KV - Impact energy (J) transverse (+A) +20° - 60 -196° - 60
KV - Impact energy (J) longitud (+A) +20° - 100

X6CrNiMoTi17-12-2 - 1.4571

A - Min elogation at fracture (%) (+A) 30 - 40
A - Min. elongation at fracture (%) longitud., (+AT) 35 - 45

X6CrNiMoTi17-12-2 - 1.4571

Nominal diameter (mm) (%) (+A) 2 - 50
Z - Z - Reduction in cross section on fracture (%) 60 - 65

X6CrNiMoTi17-12-2 - 1.4571

Birinel Sertlik (HB) (+A): 215
Birinel Sertlik (HB) (+AT): 210