X1NiCrMoCu25-20-5 - (1.4539)/904L N08904/Z2NCDU25-20/904S13/2562/00H22N24M4TCu

X1NiCrMoCu25-20-5 - 1.4539

Uygulama Bilgileri


Genel Kimliği

X1NiCrMoCu25-20-5 - 1.4539

Grade (EU) X1NiCrMoCu25-20-5
Number 1.4539
USA 904L N08904
France, ANFOR Z2NCDU25-20
England, BS 904S13
Sweden, SS 2562
Poland, PN 00H22N24M4TCu

Standartları

X1NiCrMoCu25-20-5 - 1.4539

EN 10088-2: 2005
EN 10088-3: 2005
EN 10028-7: 2007
EN 10217-7: 2005
EN 10296-2: 2005
EN 10253-3: 2008
EN 10253-4: 2008
EN 10272: 2007
EN 10250-4: 2000
EN 10297-2: 2005
EN 10088-1: 2005
EN 10088-4: 2009
EN 10088-5: 2009

Kimyasal Kompozisyonu

X1NiCrMoCu25-20-5 - 1.4539

C max 0.02
Si max 0.70
Mn max 2.00
Ni 24 - 26
P max 0.03
S max 0.01
Cr 19 - 21
Mo 4 - 5
N max 0.15
Cu 1.2 - 2

Mekanik Özellikleri

X1NiCrMoCu25-20-5 - 1.4539

Rm - Tensile strength (MPa) (+A) 520 - 730
Rm - Tensile strength (MPa) (+AT) 520 - 720

X1NiCrMoCu25-20-5 - 1.4539

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+AT) 220 - 230
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 220 - 260

X1NiCrMoCu25-20-5 - 1.4539

KV - Impact energy (J) transverse (+A) +20° - 60 -196° - 60
KV - Impact energy (J) longitud (+A) +20° - 100
KV - Impact energy (J) transverse (+A) +20° - 90 -196° - 60
KV - Impact energy (J) longitud (+A) +20° - 120

X1NiCrMoCu25-20-5 - 1.4539

A - Min elogation at fracture (%) (+A) 30 - 35
A - Min. elongation at fracture (%) transverse., (+AT) 30
A - Min. elongation at fracture (%) longitud., (+AT) 35

X1NiCrMoCu25-20-5 - 1.4539

Birinel Sertlik (HB) (+A): 230
Birinel Sertlik (HB) (+AT): 220