X2CrNiMo17-12-3 - (1.4432) / 316L / Z3CND17-13-03 / 316S13 / 2353 / 03KH17N14M3

X2CrNiMo17-12-3 - 1.4432

Uygulama Bilgileri

Korozyona karşı dirençli, Çelik şasi, -196 ° C'den düşük bir metal sıcaklığında uygulanamaz


Genel Kimliği

X2CrNiMo17-12-3 - (1.4432)

Grade (EU) X2CrNiMo17-12-3
Number 1.4432
USA 316L
Japan, JIS SUS316L
France, ANFOR Z3CND17-13-03
Z3CND18-14-03
England, BS 316S13
Sweden, SS 2353
Russia, GOST 03KH17N14M3

Standartları

X2CrNiMo17-12-3 - (1.4432)

EN 10088-2: 2005
EN 10088-3: 2005
EN 10028-7: 2007
EN 10222-5: 2000
EN 10217-7: 2005
EN 10296-2: 2005
EN 10253-3: 2008
EN 10253-4: 2008
EN 10272: 2007
EN 10263-5: 2001
EN 10088-1: 2005
EN 10088-5: 2009
EN 10088-4: 2009

Kimyasal Kompozisyonu

X2CrNiMo17-12-3 - (1.4432)

C max 0.03
Si max 1.00
Mn max 2.00
Ni 10.5 - 13
P max 0.045
S max 0.015
Cr 16.5 - 18.5
Mo 2 - 2.50
N max 0.11

Mekanik Özellikleri

X2CrNiMo17-12-3 - (1.4432)

Rm - Tensile strength (MPa) (+A) 490 - 700
Rm - Tensile strength (MPa) (+AT) 490 - 690
Rm - Tensile strength (MPa) (+AT+C) 750 - 780

X2CrNiMo17-12-3 - (1.4432)

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+AT) 190 - 240
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 190

X2CrNiMo17-12-3 - (1.4432)

KV - Impact energy (J) transverse, (+A) +20° - 60 +196° - 60
KV - Impact energy (J) longitud., (+A) +20° - 100

X2CrNiMo17-12-3 - (1.4432)

A - Min. elongation at fracture (%) (+A) 40 - 45
A - Min. elongation at fracture (%) longitud (+AT) 40

X2CrNiMo17-12-3 - (1.4432)

Nominal diameter(mm) 2 - 50
Z - Reduction in cross section on fracture (%) 63 - 68

X2CrNiMo17-12-3 - (1.4432)

Birinel Sertlik (HB) (+A): 215
Birinel Sertlik (HB) (+AT): 200