X2CrNiN23-4 - (1.4362) / S32304 / Z3CN23-04Az / 2327 / 03KH23N6
X2CrNiN23-4 - 1.4362
Uygulama Bilgileri
Grade (EU) | X2CrNiN23-4 |
Number | 1.4362 |
USA | S32304 |
France, ANFOR | Z3CN23-04Az |
Sweden, SS | 2327 |
Russia, GOST | 03KH23N6 |
EN 10088-2: 2005 |
EN 10088-3: 2005 |
EN 10028-7: 2007 |
EN 10216-5: 2014 |
EN 10217-7: 2005 |
EN 10296-2: 2005 |
EN 10253-3: 2008 |
EN 10253-4: 2008 |
EN 10272: 2007 |
EN 10263-5: 2001 |
EN 10250-4: 2000 |
EN 10297-2: 2005 |
EN 10088-1: 2005 |
EN 10088-4: 2009 |
EN 10088-5: 2009 |
C | max 0.03 |
Si | max 1.00 |
Mn | max 2.00 |
Ni | 3,5 - 5,5 |
P | max 0.035 |
S | max 0.015 |
Cr | 22 - 24 |
Mo | 0.1 - 0.6 |
N | 0.05 - 0.2 |
Cu | 0.1 - 0.6 |
Rm - Tensile strength (MPa) (+A) | 600 - 850 |
Rm - Tensile strength (MPa) (+AT) | 600 - 820 |
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+AT) | 400 |
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) | 400 - 450 |
KV - Impact energy (J) transverse (+A) | +20° - 90 | -40° - 40 |
KV - Impact energy (J) longitud (+A) | +20° 100 - 120 | |
KV - Impact energy (J) longitud (+AT) | +20° 120 |
A - Min elogation at fracture (%) (+A) | 20 - 25 |
A - Min. elongation at fracture (%) transverse., (+AT) | 25 |
A - Min. elongation at fracture (%) longitud., (+AT) | 25 |
Birinel Sertlik (HB) (+A): | 260 |
Birinel Sertlik (HB) (+AT): | 290 |