X2CrNi19-11 - (1.4306) / 304L / SUS304L / Z2CN18-10 / X2CrNi18-11 / 2352 / 00H18N10 / 720 / 03KH18N11

X2CrNi19-11 - 1.4306

Application Information


Public Id

X2CrNi19-11 - 1.4306

Grade (EU) X2CrNi19-11
Number 1.4306
USA 304L
Japan, JIS SUS304L
France, ANFOR Z2CN18-10 Z3CN18-10
England, BS 304S11
Italy, UNI X2CrNi18-11
Sweden, SS 2352
Poland, PN 00H18N10
Finland, SFS 720
Russia, GOST 03KH18N11

Standards

X2CrNi19-11 - 1.4306

EN 10088-2: 2005
EN 10088-3: 2005
EN 10028-7: 2007
EN 10216-5: 2014
EN 10217-7: 2005
EN 10296-2: 2005
EN 10253-4: 2008
EN 10272-2: 2007
EN 10263-5: 2001
EN 10250-4: 2000
EN 10297-2: 2005
EN 10253-3: 2008
EN 10088-1: 2005
EN 10088-5: 2009
EN 10088-4: 2009

Chemical Composition

X2CrNi19-11 - 1.4306

C max 0.33
Si max 1.00
Mn max 2.00
Ni 10 - 12
P max 0.045
S max 0.015
Cr 18 - 20
N max 0.11

Mechanical Properties

X2CrNi19-11 - 1.4306

Rm - Tensile strength (MPa) (+A) 460 - 700
Rm - Tensile strength (MPa) (+AT) 460 - 680
Rm - Tensile strength (MPa) (+AT+C) 740 - 780

X2CrNi19-11 - 1.4306

Rp0.2 0.2% proof strength (MPa) (+AT) 180
Rp0.2 0.2% proof strength (MPa) (+A) 180 - 220

X2CrNi19-11 - 1.4306

KV - Impact energy (J) transverse (+A) +20° - 60 -196° - 60
KV - Impact energy (J) longitud (+A) +20° - 100

X2CrNi19-11 - 1.4306

A - Min elogation at fracture (%) (+A) 35 - 45
A - Min. elongation at fracture (%) longitud., (+AT) 40

X2CrNi19-11 - 1.4306

Nominal thickness (mm) 2 - 50
Z - Reduction in cross section on fracture (%) 63 - 68

X2CrNi19-11 - 1.4306

Brinell hardness (HB) (+A): 215
Brinell hardness (HB) (+AT): 200