X6CrNiTi18-10 - (1.4541)/X10CrNiTi18-9/SUS321/Z6CNT18-10/321S31/X6CrNiTi18-11

X6CrNiTi18-10 - 1.4541

Uygulama Bilgileri


Genel Kimliği

X6CrNiTi18-10 - 1.4541

Grade (EU) X6CrNiTi18-10
Number 1.4541
USA 321
Germany, DIN X10CrNiTi18-9
Japan, JIS SUS321
France, ANFOR Z6CNT18-10
England, BS 321S31
Italy, UNI X6CrNiTi18-11
China, GB 0Cr18Ni10Ti
1Cr18Ni11Ti
H0Cr20Ni10Ti
Sweden, SS 2337
Poland, PN 0H18N10T
1H18N9T
Czechia, CSN 17247
17248
Finland, SFS 731
Austria, ONORM X6CrNiTi18-10S
Russia, GOST 08KH18N10T
08KH18N12T
12KH18N10T

Standartları

X6CrNiTi18-10 - 1.4541

EN 10088-2: 2005
EN 10088-3: 2005
EN 10028-7: 2007
EN 10222-5: 2000
EN 10216-5: 2014
EN 10217-7: 2005
EN 10296-2: 2005
EN 10253-3: 2008
EN 10253-4: 2008
EN 10272: 2007
EN 10250-4: 2000
EN 10297-2: 2005
EN 10088-1: 2005
EN 10088-4: 2009
EN 10088-5: 2009

Kimyasal Kompozisyonu

X6CrNiTi18-10 - 1.4541

C max 0.08
Si max 1.00
Mn max 2.00
Ni 9 - 12
P max 0.045
S max 0.015
Cr 17 - 19
Ti max 0.70

Mekanik Özellikleri

X6CrNiTi18-10 - 1.4541

Rm - Tensile strength (MPa) (+A) 500 - 720
Rm - Tensile strength (MPa) (+AT+C) 810 - 850
Rm - Tensile strength (MPa) (+AT) 460 - 730

X6CrNiTi18-10 - 1.4541

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+AT) 180 - 200
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 190 - 225

X6CrNiTi18-10 - 1.4541

KV - Impact energy (J) transverse (+A) +20° - 60 -196° - 60
KV - Impact energy (J) longitud (+A) +20° - 100

X6CrNiTi18-10 - 1.4541

A - Min elogation at fracture (%) (+A) 30 - 40
A - Min. elongation at fracture (%) transverse., (+AT) 35

X6CrNiTi18-10 - 1.4541

Nominal diameter (mm) (%) (+A) 2 - 50
Z - Z - Reduction in cross section on fracture (%) 60 - 65

X6CrNiTi18-10 - 1.4541

Birinel Sertlik (HB) (+A): 215
Birinel Sertlik (HB) (+AT): 210