X5CrNi18-10 - (1.4301) / SUS 304 / X5CrNi18-9 / 301S21 / 0Cr18Ni9 / 17240 / 725

X5CrNi18-10 - 1.4301

Uygulama Bilgileri


Genel Kimliği

X5CrNi18-10 - 1.4301

Grade (EU) X5CrNi18-10
Number 1.4310
Density 7.9 g/cm³
USA 304 - 304N
Germany, DIN X5CrNi18-9
Japan, JIS SUS304
France, ANFOR X5CrNi18-10
Z5CN18-09
Z6CN18-09
Z7CN18-09
England, BS 301S21
302S26
Italy, UNI X5CrNi18-10
China, GB 0Cr18Ni9
Sweden, SS 2333-02
Poland, PN 0H18N9
Czechia, CSN 17240
Finland, SFS 725
Austria, ONORM X5CrNi18-10S

Standartları

X5CrNi18-10 - 1.4301

EN 10088-2: 2005
EN 10088-3: 2005
EN 10028-7: 2007
EN 10222-5: 2000
EN 10151: 2003
EN 10216-5: 2014
EN 10217-7: 2005
EN 10296-2: 2005
EN 10253-3: 2008
EN 10253-4: 2008
EN 10269-4: 1999
EN 10272: 2007
EN 10263-5: 2001
EN 10250-4: 2000
EN 10297-2: 2005
EN 10088-4: 2009
EN 10088-5: 2009

Kimyasal Kompozisyonu

X5CrNi18-10 - 1.4301

C MAX 0.07
Si max 1.00
Mn max 2.00
Ni 8 - 10.5
P max 0.045
S max 0.015
Cr 17.5 - 19.5
N max 0.11

Mekanik Özellikleri

X5CrNi18-10 - 1.4301

Rm - Tensile strength (MPa) (+A) 500 - 750
Rm - Tensile strength (MPa) (+AT) 500 - 700
Rm - Tensile strength (MPa) (+AT+C) 780 - 820

X5CrNi18-10 - 1.4301

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+At) 195
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 190 - 235

X5CrNi18-10 - 1.4301

KV - Inpact energy (J) transverse (+A) +20° - 60 -196° - 60
KV - Inpact energy (J) longitud (+A) +20° - 100

X5CrNi18-10 - 1.4301

A - Min. elongation at fracture (%) (+A) 35 - 45
A - Min. elongation at fracture (%) longitud 40

X5CrNi18-10 - 1.4301

Vickers Sertlik (HV) (+CR): 220 - 450
Brinell Sertlik (HB) (+A): 215
Brinell Sertlik (HB) (+AT): 200